Beam splitter divides or combines beams with desired transmittance and reflectance in a required wavelength region, or divides beam light into the P-polarization and S-polarization components.
1,45°Beam Splitters
Substrate: Fused silica, BK7 
Surface Figure: <λ/10 @ 632.8nm
Surface Quality: 40-20
Chamfer: 0.5mm×45°
Coating Material: Electron beam deposited dielectric: multi-layers
Incident: 0°,45°
Laser-Induced Damage Threshold: >5J/cm2 (1.06μm,1ns)
| Incident Angle | Wavelength (nm) | Separating | Tolerance | ||
| Tave/Rave | Tp/Rp | Tp/Rp | |||
| 45° | 510-500 | 50/50 | ±3% | ||
| 45° | 780 | 50/50 | ±3% | ||
| 45° | 632.8 | 50/50 | ±3% |
2,Polarizing Beam splitter Plates
Substrate Fused: silica, BK7 
Surface Figure: <λ/10 @ 632.8nm
Surface Quality: 40-20
Chamfer: 0.5mm×45°
Coating Material: Electron beam deposited----------dielectric multi-layers
AOI: 56.6°±3°
Polarizing: Tp≥96%; Ts≤1%
Extinction Ratio: Tp:Ts>100:1
Wavelength Range: Visible, Near Infrared
| Wavelength(nm) | Wavelength(nm) |
| 20/25.4/30 | 780 |
| 20/25.4/30 | 1064 |
| 20/25.4/30 | 1310 |
| 20/25.4/30 | 1550 |
3,Dichroic Beam Splitters
Substrate: Fused silica, BK7 
Surface Figure: <λ/10 @ 632.8nm
Surface Quality: 40-20
Chamfer: 0.5mm×45°
Coating Material: Electron beam deposited dielectric: multi-layers
Incident: 0°,
Laser-Induced Damage Threshold: >5J/cm2 (1.06μm,1ns)
| Incident Angle | TWavelength (nm) | Transmission | RWavelength | Reflectance |
| 0° | 808 | >90% | 946 | >99.5% |
| 0° | 808 | >90% | 1064 | >99.5% |
| 0° | 808 | >90% | 1320 | >99.5% |
| 0° | 940 | >90% | 1030 | >99.5% |
4，Polarizing Beam splitters Cubes
Substrate: Fused: silica, BK7 
Surface Figure: <λ/10 @ 632.8nm
Surface Quality: 40-20
Chamfer: 0.5mm×45°
Coating Material: Electron beam deposited dielectric: multi-layers
Incident:0°±2°
Polarizing: Tp≥98%; Ts≤0.2%
Extinction Ratio: Tp:Ts>500:1
AR Coating: R<0.25%
| Wavelength (nm) |
| 632.8 |
| 780 |
| 830 |
| 852 |
| 1064 |
| 1310 |
| 1550 |
| 420-470 |